Sanitary epoxy polyamide procedure

E-color sanitary epoxy paint is an epoxy-poly-hope two-component primer. This paint is also approved for use in sanitary departments and drinking water systems.

Description of solvent-free sanitary epoxy primer

Its properties include:

Very good corrosion resistance
High chemical resistance
High abrasion resistance and hardness
Excellent water and moisture resistance
Good adhesion to steel surfaces
Applicable with thicknesses over 200 microns
Surface impermeability
Designed for health systems
Shine and excellent appearance

Uses

This coating is used alone as the final layer of sanitary epoxy systems and drinking water to protect the surfaces against corrosion and microbes. Due to the high solid percentage of paint with a spraying step, thicknesses up to 500 microns can be achieved. Its uses include:

Drinking water tanks
Water transfer pipes
Sanitary equipment
Industrial Drug Making Machines
Food Equipment
Food storage cells
Sanitary ware containers
Clean hall and operating room flooring

Technical specifications

فام td>	White (other shades suggested subject to conditions)
Volume solid percentage	100
Storage time	one year
Recommended thickness	500 to 200 microns
Density	05, 0 ± 1.53
50 micron theory cover	1.5 square meters per kilogram
Theoretical coverage of 100 microns per liter	6 m2 / td>

Drying and coating conditions

Drying time				Next layer application time
Temperature	surface	practical	Complete hardening	minimum	Maximum	Notes
25 ° C	4 hours	24 hours	7 days	12 to 24 hours	6 days	Other factors such as the thickness of the color film and temperature changes, etc. affect the drying time.

Terms and equipment of application

Thinner	TEP (Epoxy Thinner)
Application temperature	5 to 50 degrees Celsius
Maximum relative humidity	80%
Surface temperature	3 to 5 degrees above the dew point
Application method	Air spray. Airless spray, brush and roll
useful life of paint and hardener mixture	1 hour at 20 ° C

Application conditions	Ordinary spray	Airless spray	brush	Roll
Percent solvent	15-10%	8-5%	9-6%	9-6%
head pressure	4-6 times	120-160 times
Nozzle head diameter	1.6 to 1.8 mm	0.35 to 0.5 mm
hand distance	30-50%	40-60 cm

Surface preparation

Painted surfaces – These surfaces must be completely clean and free of any grease and other contaminants. Before painting, the surface should be completely dry and if a long time has passed since the application of the undercoat, a suitable roughness should be created by soft sanding on the surface. Steel surfaces – Wash the steel surface with a suitable solvent to remove grease, salt and any other contaminants. De-rust and create profiles on surfaces by various methods such as sand blasting up to 2.5 degrees Swedish or by mechanical tools up to ISO-ST3 degree. In metal structures and welded points and corners should be smooth and polished and free of any appendages and sharpness. After de-rusting and creating a profile, remove the particles from the preparation and other contaminants from the surface with a pressure of air free of moisture and grease and with the method of vacuum and thoroughly clean. Note that the application of the first layer (primer) should be done no later than two hours after preparation. Concrete surfaces – If the concrete is fresh, it must be 28 days after the concrete has been applied (the concrete surface is completely dry). If the concrete is old, the surface must be washed with fresh water to remove contaminants such as salts, grease, dust and Dust, loose and unstable particles, etc. from its surface

Description of hygienic polyamide epoxy procedure

Its properties include:

High flexibility
High chemical resistance
High abrasion resistance and hardness
Excellent water and moisture resistance
Good adhesion to aluminum, steel and other metal surfaces
Applicable over 100 microns thick
Surface impermeability
Self-cleaning capability
Designed for health systems

Uses

This coating is used alone as the final layer of sanitary epoxy systems and drinking water to protect the surfaces against corrosion and microbes. Due to the high solid percentage of paint with a spraying step, a high thickness can be achieved. Its uses include:

Drinking water tanks
Water transfer pipes
Sanitary equipment
Industrial Drug Making Machines
Food Equipment
Food storage cells
Sanitary ware containers

Technical specifications

فام td>	White (other shades suggested subject to conditions)
Volume solid percentage	60 ± 2
Storage time	one year
Recommended thickness	100 microns
Density	05, 0 ± 1.35
Number of components	Two components
100 micron theory coverage	4.3 square meters per kilogram
Theoretical coverage of 100 microns per liter	6 m2 / td>
percentage by weight	75 ± 1
Number of components	Two components
weight ratio of components	86% of the first component and 14% of the second component (hardener)
Volume mixing ratio of components	79% of the first component and 21% of the second component (hardener)

Drying and coating conditions

Drying time				Next layer application time
Temperature	surface	practical	Complete hardening	minimum	Maximum	Notes
25 ° C	4 hours	24 hours	7 days	12 to 24 hours	6 days	Other factors such as the thickness of the color film and temperature changes, etc. affect the drying time.

Terms and equipment of application

Thinner	TEP (Epoxy Thinner)
Application temperature	5 to 50 degrees Celsius
Maximum relative humidity	80%
Surface temperature	3 to 5 degrees above the dew point
Application method	Air spray. Airless spray, brush and roll
useful life of paint and hardener mixture	8 hours at 20 ° C

Application conditions	Ordinary spray	Airless spray	brush	Roll
Percent solvent	15-10%	8-5%	9-6%	9-6%
head pressure	4-6 times	120-160 times
Nozzle head diameter	1.6 to 1.8 mm	0.35 to 0.5 mm
hand distance	30-50%	40-60 cm

Surface preparation